Product Description
A new edition of this all-time classic. Made of 100% polyester, Vintage Three-Strand looks like a traditional filament rope, but behaves like state-of-the-art cordage. Its advantages include a long service life and low stretch. Use Vintage Three-Strand as sheets, in tackles, as multipurpose rope and for decorative purposes. Stretch: 9.90% at 20% of breaking strength.
Features:
- New England Ropes "Vintage" Tan 3-Strand Polyester Line is the perfect compliment for the traditional vessel
- Excellent abrasion resistance
- Low stretch
- High strength
- Easy to splice
- Material: Polyester
- Applications:
- Halyards
- Control Lines
- Anchor and Dock lines
- Great for Nautical Themed Decorative Use
- Colors Available: Natural / Tan
- Sunlight / UV: Very little degradation from sunlight
- Can be used outside over long term if inspected regularly
- Chemicals: Polyester has good resistance to most chemicals except 95% sulfuric acid and strong alkalines at boil
- Heat: Polyester melts at 480° F with progressive strength loss above 300° F
- Dielectrics: Good resistance to the passage of electrical current
- However, dirt, surface contaminants, water entrapment, and the like can significantly affect dielectric properties
- Extreme caution should be exercised any time a rope is in the proximity of live circuits
- Sheaves:
- Recommended sheave diameter to rope diameter is 8:1
TECHNICAL DATA:
Diameter [mm] | Diameter [inch] | Circumference [inch] | Weight [g/m] | Weight [lbs/100'] | min. Breaking strength [lbf] | Avg. Breaking strength |
6 | 1/4 | 24,8 | 1,7 | 1.450 | ||
8 | 5/16 | 38,8 | 2,6 | 2.100 | ||
10 | 3/8 | 65,5 | 4,4 | 3.450 | ||
11 | 7/16 | 76,2 | 5,1 | 4.150 | ||
12 | 1/2 | 108,6 | 7,3 | 6.200 | ||
16 | 5/8 | 165,1 | 11,1 | 8.100 | ||
18 | 3/4 | 245,5 | 16,5 | 11.000 | ||
24 | 1 | 461,2 | 31 | 20.000 |